Product Name: 201 cold-rolled stainless steel coil
Brief Introduction: 201 stainless steel coil is a nickel-saving austenitic stainless steel, with a typical composition of 13.5%-17.5% chromium, 1.0%-1.8% nickel, and 5.5%-7.5% manganese. Its properties are similar to 304, but it is non-magnetic, has slightly weaker corrosion resistance, and is significantly cheaper. Its strength can be improved through work hardening.
Application:
Mechanical Properties:
| Property | Value |
| Tensile Strength | 520-758MPa |
| Yield Strength | 275-350MPa |
| Elongation | 40-60% |
| Hardness | ＜183 HB |
| Elastic Modulus | 200GPa |
| Poisson’s Ratio | 0.3 |
Chemistry Composition
| Element | Percentage |
| Chromium(Cr) | 16-18% |
| Nickel(Ni) | 3.5-5.5% |
| Carbon（C） | 0.15%（max） |
| Manganese（Mn） | 5.5-7.5%（max） |
| Silicon（Si）） | 0.75-1.00%（max） |
| Phosphorus(P) | 0.06%（max） |
| Sulfur（S） | 0.03%（max） |
Mechanical Properties:
| Property | Value |
| Tensile Strength | 520-758MPa |
| Yield Strength | 275-350MPa |
| Elongation | 40-60% |
| Hardness | ＜183 HB |
| Elastic Modulus | 200GPa |
| Poisson’s Ratio | 0.3 |
Chemistry Composition
| Element | Percentage |
| Chromium(Cr) | 16-18% |
| Nickel(Ni) | 3.5-5.5% |
| Carbon（C） | 0.15%（max） |
| Manganese（Mn） | 5.5-7.5%（max） |
| Silicon（Si）） | 0.75-1.00%（max） |
| Phosphorus(P) | 0.06%（max） |
| Sulfur（S） | 0.03%（max） |